التسخين الومضي لمانع التآكل القائم على الإيبوكسي أغشية رقيقة على ركائز الألومنيوم

The following investigation shows the experimental evaluation of a transient heat load centered on a corrosion inhibitor coating employed in the epoxy polyamide primary. The temperature at which the epoxy polyamide film initiated thermal deterioration increased with increased heating rates. This coating is a Deft Inc.’s high- quality solid epoxy primary. A single inch diameter lamp on two types of aluminum substrates was focused on the xenon flashlight: AA2024- T4 and AA7075- T3. For modeling purposes, edge effects have not been explored. The ceramic firebrick isolated the coated aluminum disks to ensure minimum edge effects. The FTCS model has been designed to calculate the temporary reaction to the thermal energy flash load. It has been demonstrated that substrates have a substantial impact on epoxy polyamide film energy absorption, film surface temperatures and absorbed energy. Keywords: flash heating, corrosion inhibitor, aluminum substrates, epoxy.

يوضح البحث التالي التقييم التجريبي للحمل الحراري العابر المتمركز على طلاء مانع للتآكل مستخدم في مادة البولي إيبوكسي الأولية. عندما نقوم بزيادت درجة الحرارة التي بدأ عندها فيلم الإيبوكسي بولي أميد التدهور الحراري حيث تزداد معدلات التسخين. ان هذا الطلاء هو ذات جودة عالية الإيبوكسي لشركة حاذق في صلب الابتدائي.حيث نقوم بتركيز مصباح قطرهه بوصة واحدة على نوعين من ركائز الألومنيوم على مصباح زينون: AA2024- T4 و T3 AA7075- . لنمذجة الأغراض، لم تستكشف آثار الحافة. عزل الطوب الناري الخزفي أقراص الألمنيوم المطلية لضمان الحد الأدنى من تأثيرات الحواف. تم تصميم نموذج FTCS لحساب التفاعل المؤقت لحمولة فلاش الطاقة الحرارية. لقد اثبت أن الركائز لها تأثير كبير على امتصاص طاقة غشاء بولي أميد الإيبوكسي ودرجات حرارة سطح الفيلم والطاقة الممتصة. الكلمات المفتاحية: التخسين الومضي – مانع التآكل – ركائز الألومنيوم – الإيبوكسي.