Synthesis of azo polymers by etheric derivatives polymerization of allyl bromide and studying their bandgap and determine some of their properties
Ghazi Mahmoud Hasso Jawish
Rushdi Madwar
Faculty of Science || Al-Baath University || Syria
Francois Kara Bet
Faculty of Science || Damascus University || Syria
Tab title In this research, two ether derivatives of phenolic azo dyes were synthesized via Williamson’s reaction according to the SN2 mechanism. The prepared compounds were radically polymerized using (AIBN) as an initiator and their structures were identified by FT-IR and 1H-NMR. Furthermore, thermal properties of these polymers was made by (DSC). Bandgap energy have been calculated to indicate the ability of these polymers as optical semiconductors, it was 2.8ev, 2.4ev for P(AO2) and P(AON1) respectively. Beside the determination of refractive index, kinematic viscosity, density, and degree of Turbidity. Keywords: Azo polymer, Williamson reaction, radically polymerized, AIBN, etheric derivatives, bandgap, DSC.
Tab title
In this research, two ether derivatives of phenolic azo dyes were synthesized via Williamson’s reaction according to the SN2 mechanism. The prepared compounds were radically polymerized using (AIBN) as an initiator and their structures were identified by FT-IR and 1H-NMR. Furthermore, thermal properties of these polymers was made by (DSC). Bandgap energy have been calculated to indicate the ability of these polymers as optical semiconductors, it was 2.8ev, 2.4ev for P(AO2) and P(AON1) respectively. Beside the determination of refractive index, kinematic viscosity, density, and degree of Turbidity. Keywords: Azo polymer, Williamson reaction, radically polymerized, AIBN, etheric derivatives, bandgap, DSC.
اصطناع بوليميرات آزو ببلمرة مشتاقات إيتيرية لبروميد الآليل ودراسة فجوتها الطاقية وتعيين بعض خصائصها الفيزيائية
غازي محمود حسو جاويش
رشدي مدور
كلية العلوم || جامعة البعث || سوريا
فرانسوا قره بت
كلية العلوم || جامعة دمشق || سوريا
Tab title
في هذا البحث، اُصطنع مشتقان ايتريين لاصبغة ازو فينولية عن طريق تفاعل ويليمسون وفقاً لآلية. الاستبدال النيكلوفيلي SN2. تمت بلمرة المركبات المحضرة بلمرةً جذرية باستخدام (AIBN) كبادئ وأُثبتت بنى المركبات المصطنعة بواسطة مطيافيات FT-IR و 1H-NMR. بالإضافة إلى دراسة الخصائص الحرارية للبوليميرات المُحضرة بواسطة (DSC). دُرست عرض الفجوة الطاقية وذلك لمعرفة امكانية استعمال البوليميرات كأنصاف نواقل ضوئية وكانت قيمتها 2.4ev, 2.8ev لكل من P(AO2) و P(AON1) على التوالي. كماعُينت كل من قرينة الانكسار واللزوجة الكيناميكية والكثافة ودرجة العكارة. الكلمات المفتاحية: بوليميرات الآزو، مشتقات إيتيرية، تفاعل وليمسون، بلمرة جذرية، AIBN، فجوة الطاقة، لزوجة كيناميكية، DSC.