Preparation of Semipermeable polyvinylpyrrolidone Membranes and Study Their Chemical, Physical and Mechanical Properties

Khatoon Khalil Al-Hamad

Fawaz Ahmad Al- Deri

Ahmad Mohamd Al-Falah

Faculty of Sciences || Damascus University || Syria

DOI PDF

Been we had prepared three semipermeable membranes with different concentration of polyvinylpyrrolidone by the phase inversion process. This way is a basic method to get flat membranes. the membranes were tested for chemical properties (pH rang), and physical properties (viscosity and porosity), and mechanical properties (tensile strength and strain), The results showed that polyvinylpyrrolidone (8%, 12% ,15%) membrane having the higher pH rang, while the polyvinylpyrrolidone (15%) membrane having the higher tensile strength and strain, but it was having the lowest porosity, viscosity was measured in low concentration was showed that polyvinylpyrrolidone (2%) solution having the higher viscosity. Keywords: Semipermeable membrane of polyvinylpyrrolidone, Phase inversion process.

تحضير أغشية نصف نفوذه من بولي فينيل بيروليدون ودراسة خواصها الكيميائية والفيزيائية والميكانيكية

خاتون خليل الحمد

فواز أحمد الديري

أحمد محمد الفلاح

كلية العلوم || جامعة دمشق || سوريا

تم تحضير ثلاثة أغشية مختلفة التركيز من بولي فينيل بيروليدون باستخدام طريقة تحول الحالة وتعتبر هذه الطريقة أساس في الحصول على أغشية مستوية. ودرست الخواص الكيميائية وهي (مجال ال pH)، والخواص الفيزيائية وهي (اللزوجة والمسامية)، والخواص الميكانيكية (قوة الشد والانفعال)، وقد أظهرت النتائج أن غشاء بولي فينيل بيروليدون عند التراكيز (8%, 12%, 15%) تحمل تغيرات مجال  3- 5)=(pH، في حين أن غشاء بولي فينيل بيروليدون ذي التركيز (15%) كان الأعلى من حيث قوة الشد والانفعال، لكنه كان الأدنى من حيث المسامية، وتم قياس اللزوجة عند التراكيز المنخفضة وكان التركيز (2%) هو الأعلى من حيث اللزوجة. الكلمات المفتاحية: غشاء نصف نفوذ من بولي فينيل بيروليدون، طريقة تحول الحالة.

==> أرسل بحثك <==